Performance and characteristics: Cr3C2=180.02, carbon content 13.34%, gray powder, orthorhombic crystal structure, insoluble in water, resistant to acid and alkali. Density is 6.65-6.68 g/cm3, melting point: 1890 degrees, boiling point
Performance and characteristics: Cr3C2=180.02, carbon content 13.34%, gray powder, orthorhombic crystal structure, insoluble in water, resistant to acid and alkali. Density is 6.65-6.68 g/cm3, melting point: 1890 degrees, boiling point
性能与特点：Cr3C2 = 180.02，碳含量13.34％，灰色粉末，斜方晶体结构，不溶于水，耐酸碱。密度为6.65-6.68 g / cm3，熔点：1890度，沸点
Properties and Characteristics: Cr3C2 = 180.02, 13.34% carbonaceous as a gray powder, the crystal structure of the swash square, insoluble in water, resistant to acid density of 6.65-6.68 g / cm 3, melting point: 1890 degrees, the boiling point
性质与特性：Cr3C2 = 180.02，含碳量为灰绿色粉末，为13.34％，斜方晶体结构，不溶于水，耐酸密度为6.65-6.68 g / cm 3，熔点：1890度，沸点
无法加载全部结果
重试
正在重试…
正在重试…
: 3800 degrees.
: 3800 degrees.
...
无法加载全部结果
重试
正在重试…
正在重试…
It is a high-melting inorganic material with good wear resistance, corrosion resistance and oxidation resistance in a high temperature environment (1000-1100 degrees). It is widely used as a thermal spray material for metal surface protection, and it is also commonly used as a cemented carbide
It is a high-melting inorganic material with good wear resistance, corrosion resistance and oxidation resistance in a high temperature environment (1000-1100 degrees). It is widely used as a thermal spray material for metal surface protection, and it is also commonly used as a cemented carbide
It is a (1000-1100 degrees) in a high temperature environment having a good wear, corrosion, oxidation of the high-melting inorganic material, widely used as thermal spray material is protected metal surface, also commonly used as carbide
The grain refiner and other wear-resistant and corrosion-resistant components.
The grain refiner and other wear-resistant and corrosion-resistant components.
晶粒细化剂和其他耐磨，耐腐蚀的部件。
grain refining agents and other wear and corrosion resistance element.
晶粒细化剂和其他耐磨和抗腐蚀元素。
无法加载全部结果
重试
正在重试…
正在重试…
The Cr3C2-based cermet has excellent oxidation resistance at high temperatures, and the surface is only slightly darkened after being exposed to heat at 982°C for 5 hours.
The Cr3C2-based cermet has excellent oxidation resistance at high temperatures, and the surface is only slightly darkened after being exposed to heat at 982°C for 5 hours.
In Cr3C2 cermet base has very excellent oxidation resistance at high temperatures After 5 hours at 982 deg.] C heat exposure, only slightly darkened surface.
Performance and characteristics: Cr3C2=180.02, carbon content 13.34%, gray powder, orthorhombic crystal structure, insoluble in water, resistant to acid and alkali. Density is 6.65-6.68 g/cm3, melting point: 1890 degrees, boiling point