Stellite F Co Based Alloy Powder Plasma Surfacing Laser Cladding Powder Metallurgy Products

       

Stellite F Co Based Alloy Powder is Co alloy
powder with high content of W, so the hardness is high. The surfacing layer has
good corrosion resistance, heat resistance and wear resistance, which can be
maintained at 800 ℃.

Name: Stellite F cobalt based alloy powder

Standard: AWS a5013-rcocr-b

Application: used for the blade with strong
abrasive wear, such as plastic, paper and chemical raw materials. Pre
protection of blade edge and surfacing of valve sealing surface and exhaust
valve cone of internal combustion engine. Stellite alloy castings are suitable
for nuclear power, petrochemical, electric power, battery, glass, light
industry, food and many other fields. It has the characteristics of wear resistance,
corrosion resistance, oxidation resistance and high temperature resistance.
Commonly used products are valve core, valve seat, shaft, shaft sleeve, pump
parts, glass, battery mold, nozzle and cutting tool. Alloy categories are: Co
based alloy casting, Ni based alloy casting, Fe based alloy casting. Stellite
powder metallurgy products are made of Co based, Ni based or Fe based alloy
atomized powder by pressing, sintering and finishing. The main products are
valve stem, valve core (ball), valve seat, valve ring, sealing ring, wood saw
tooth, bearing pump, bearing ball, etc.

Hardness: HRC ≥ 42

Weight: 5kg / bottle

Process: suitable for plasma powder
surfacing process.

Note: if the alloy powder has moisture
absorption, or the storage period is more than 3 months, it should be stored
before use

Drying treatment (150 ℃ for 2 hours)

The cobalt based alloy powder produced by
wococarbide is suitable for plasma surfacing, laser cladding and oxyacetylene
spray welding. The cobalt base spray welding alloy powder described below is
packaged in plastic bucket and iron bucket. However, due to the fine powder
particles, it is easy to absorb moisture. It is recommended that the user
should keep the temperature at 120 ℃ for two hours before use, and then use it
after drying.