Iron based powder

       Brand name Chemical composition Preparation method Particle size range Typical application data download
WOCO156 Iron-Molybdenum-Aluminum Powder AP Fe3Al3 Mo3CB Agglomerated Repair of 115/45μm Iron-Based Parts, Crankshaft Journal Connecting Rod. Working temperature<360℃ --
WOCO159 Iron Chromium Molybdenum Powder HV Fe17Cr11Mo 3Ni3Si3Cu4B Agglomerated 45/6μm Iron-based wear-resistant and corrosion-resistant coating, relatively inexpensive, can be used to replace chrome plating. Can be used for crankshafts, hydraulic rods. Working temperature<500℃ --
WOCO161 Iron-Molybdenum Carbon Powder HV Fe30Mo2C Agglomerated 45/6μm Low-cost substitute for hard chrome plating and repair of cast iron parts, wear-resistant particle wear, hard bearing surface, micro-vibration resistance. Working temperature<350℃ --
WOCO162 Fe-Ni-Al powder AP Fe37Ni6Al Agglomeration 106/45μm Exothermic reaction occurs when spraying, forming strong metallurgical bond with the substrate, the coating can be processed, the coating is resistant to high temperature corrosion, the working temperature is <800℃ --
WOCO163 Iron Nickel Molybdenum Powder CP Fe35NiMoA Agglomerated 125/45μm Iron-based Parts Repair, Diesel Engine Parts, Diesel Engine Ignition Plate and Cylinder Head, High Temperature Oxidation and Wear Resistance, Working Temperature <800℃ --
WOCO165 Iron Tungsten Nickel Powder AP Fe14WNiCr Agglomerated 115/45μm High Shear Strength, Used for Friction Plates of Tanks and Bulldozers, Automobile Synchronizers, Working Temperature <500℃ --
WOCO166C Iron Chromium Boron Powder CF LC Fe20Cr7B0.5Si Gas atomization 175/89μm High density, high hardness, wear resistance, high temperature oxidation resistance, working temperature up to 980℃ --
WOCO166F Iron-chromium-boron powder CP Fe20Cr7B0.5Si Gas atomization 106/45μm High density, high hardness, wear resistance, high temperature oxidation resistance, working temperature up to 980 ℃, plastic industry extrusion screw wear layer --